Tipo: | Dissertação |
Título: | FUNCIONALIZAÇÃO DE NANOLÂMINAS DE ÓXIDO DE GRAFENO POR MEIO DE ÁCIDO OXÁLICO E DOPADAS COM CÁLCIO PARA APLICAÇÃO EM ARGAMASSAS DE CIMENTO PORTLAND – PROPRIEDADES FÍSICAS E MECÂNICAS |
Título(s) alternativo(s): | Functionalization of graphene oxide nanoslides by oxalic acid and dopped with calcium for Portland cement mortars - Physico and mechanical properties |
Autor(es): | Baldin, Victor |
Primeiro Orientador: | Felipe, Alexsandro dos Santos |
Primeiro Coorientador: | Castro, Carlos Frederico de Souza |
metadata.dc.contributor.advisor-co2: | do Carmo, Devaney Ribeiro |
Primeiro Membro da Banca: | dos Reis, Idalci Cruvinel |
Segundo Membro da Banca: | Sato, Flavio Hiochio |
Resumo: | Diversas pesquisas utilizaram o óxido de grafeno como aditivo para aprimorar as propriedades mecânicas dos compostos cimentícios, assim como têm buscado melhorias para o próprio nanomaterial por meio de modificações estruturais em sua superfície. Colaborando com essa tendência, essa pesquisa visa sintetizar o óxido de grafeno, tratá-lo quimicamente com ácido oxálico e dopá-lo com cálcio para posterior adição em argamassas de cimento Portland em 0,03% da massa de cimento. Para comparar os benefícios encontrados por esse procedimento, confeccionou-se três composições: amostras de referência (sem adições), com adição do óxido de grafeno, e com óxido de grafeno funcionalizado e dopado. Avaliou-as por meio de ensaios mecânicos de resistência à compressão e tração na flexão, absorção de água e variação dimensional. Para todas as propriedades estudadas, comparando as três composições, notou-se êxito nas sínteses químicas, com isso, os melhores resultados foram obtidos para as amostras dopadas com cálcio, com ganhos de 15,93% e 13,91% na resistência à compressão, aos 7 dias e 28 dias, respectivamente, e para a resistência à tração na flexão 15,89% e 27,14%, aos 7 dias e 28 dias, respectivamente. Para a microestrutura, notou-se que houve uma melhoria no refinamento dos poros, gerando uma compactação da matriz, desta forma, verifica-se que a proposta se tornou eficiente no aprimoramento das propriedades de resistência mecânica. |
Abstract: | Several studies have used graphene oxide as an additive to improve the mechanical properties of cementitious compounds, as well as have sought improvements to the nanomaterial itself through structural modifications to its surface. Collaborating with this trend, this research aims to synthesize graphene oxide, treat it chemically with oxalic acid and dope it with calcium for later addition in Portland cement mortars in 0.03% of the cement mass. To compare the benefits found by this procedure, three compositions were made: reference samples (without additions), with addition of graphene oxide, and with functionalized and doped graphene oxide. They were evaluated by means of mechanical tests of compressive and tensile strength in bending, water absorption and dimensional variation. For all the properties studied, comparing the three compositions, there was success in the chemical syntheses, with this, the best results were obtained for the samples doped with calcium, with gains of 15.93% and 13.91% in the compression resistance, at 7 days and 28 days, respectively, and for tensile strength at bending 15.89% and 27.14%, at 7 days and 28 days, respectively. For the microstructure, it was noticed that there was an improvement in the refinement of the pores, generating a compaction of the matrix, thus, it is verified that the proposal became efficient in the improvement of the properties of mechanical resistance. |
Palavras-chave: | Funcionalização Dopagem Argamassa Alótropos de Carbono |
Área do CNPq: | CNPQ::ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL::MATERIAIS E COMPONENTES DE CONSTRUCAO |
Idioma: | por |
Pais: | Brasil |
Editor: | Instituto Federal Goiano |
Sigla da Instituição: | IF Goiano |
Campus: | Campus Rio Verde |
Programa/Curso: | Programa de Pós-Graduação em Engenharia Aplicada e Sustentabilidade |
Tipo de Acesso: | Acesso Restrito |
metadata.dc.rights.uri: | http://creativecommons.org/licenses/by-nc-nd/3.0/br/ |
URI: | https://repositorio.ifgoiano.edu.br/handle/prefix/1966 |
Data do documento: | 8-Jan-2021 |
Aparece nas coleções: | Mestrado em Engenharia Aplicada e Sustentabilidade |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Dissertação_Victor Baldin.pdf | 1,81 MB | Adobe PDF | Visualizar/Abrir |
Este item está licenciada sob uma Licença Creative Commons