Title: FUNCIONALIZAÇÃO DE NANOLÂMINAS DE ÓXIDO DE GRAFENO POR MEIO DE ÁCIDO OXÁLICO E DOPADAS COM CÁLCIO PARA APLICAÇÃO EM ARGAMASSAS DE CIMENTO PORTLAND – PROPRIEDADES FÍSICAS E MECÂNICAS
Other Titles: Functionalization of graphene oxide nanoslides by oxalic acid and dopped with calcium for Portland cement mortars - Physico and mechanical properties
metadata.dc.creator: Baldin, Victor
metadata.dc.contributor.advisor1: Felipe, Alexsandro dos Santos
metadata.dc.contributor.advisor-co1: Castro, Carlos Frederico de Souza
metadata.dc.contributor.advisor-co2: do Carmo, Devaney Ribeiro
metadata.dc.contributor.referee1: dos Reis, Idalci Cruvinel
metadata.dc.contributor.referee2: Sato, Flavio Hiochio
metadata.dc.description.resumo: Diversas pesquisas utilizaram o óxido de grafeno como aditivo para aprimorar as propriedades mecânicas dos compostos cimentícios, assim como têm buscado melhorias para o próprio nanomaterial por meio de modificações estruturais em sua superfície. Colaborando com essa tendência, essa pesquisa visa sintetizar o óxido de grafeno, tratá-lo quimicamente com ácido oxálico e dopá-lo com cálcio para posterior adição em argamassas de cimento Portland em 0,03% da massa de cimento. Para comparar os benefícios encontrados por esse procedimento, confeccionou-se três composições: amostras de referência (sem adições), com adição do óxido de grafeno, e com óxido de grafeno funcionalizado e dopado. Avaliou-as por meio de ensaios mecânicos de resistência à compressão e tração na flexão, absorção de água e variação dimensional. Para todas as propriedades estudadas, comparando as três composições, notou-se êxito nas sínteses químicas, com isso, os melhores resultados foram obtidos para as amostras dopadas com cálcio, com ganhos de 15,93% e 13,91% na resistência à compressão, aos 7 dias e 28 dias, respectivamente, e para a resistência à tração na flexão 15,89% e 27,14%, aos 7 dias e 28 dias, respectivamente. Para a microestrutura, notou-se que houve uma melhoria no refinamento dos poros, gerando uma compactação da matriz, desta forma, verifica-se que a proposta se tornou eficiente no aprimoramento das propriedades de resistência mecânica.
Abstract: Several studies have used graphene oxide as an additive to improve the mechanical properties of cementitious compounds, as well as have sought improvements to the nanomaterial itself through structural modifications to its surface. Collaborating with this trend, this research aims to synthesize graphene oxide, treat it chemically with oxalic acid and dope it with calcium for later addition in Portland cement mortars in 0.03% of the cement mass. To compare the benefits found by this procedure, three compositions were made: reference samples (without additions), with addition of graphene oxide, and with functionalized and doped graphene oxide. They were evaluated by means of mechanical tests of compressive and tensile strength in bending, water absorption and dimensional variation. For all the properties studied, comparing the three compositions, there was success in the chemical syntheses, with this, the best results were obtained for the samples doped with calcium, with gains of 15.93% and 13.91% in the compression resistance, at 7 days and 28 days, respectively, and for tensile strength at bending 15.89% and 27.14%, at 7 days and 28 days, respectively. For the microstructure, it was noticed that there was an improvement in the refinement of the pores, generating a compaction of the matrix, thus, it is verified that the proposal became efficient in the improvement of the properties of mechanical resistance.
Keywords: Funcionalização
Dopagem
Argamassa
Alótropos de Carbono
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL::MATERIAIS E COMPONENTES DE CONSTRUCAO
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Instituto Federal Goiano
metadata.dc.publisher.initials: IF Goiano
metadata.dc.publisher.department: Campus Rio Verde
metadata.dc.publisher.program: Programa de Pós-Graduação em Engenharia Aplicada e Sustentabilidade
metadata.dc.rights: Acesso Restrito
metadata.dc.rights.uri: http://creativecommons.org/licenses/by-nc-nd/3.0/br/
URI: https://repositorio.ifgoiano.edu.br/handle/prefix/1966
Issue Date: 8-Jan-2021
Appears in Collections:Mestrado em Engenharia Aplicada e Sustentabilidade

Files in This Item:
File Description SizeFormat 
Dissertação_Victor Baldin.pdf1,81 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons