Title: Produção de briquetes de resíduo de madeira de eucalipto de agroindústrias
metadata.dc.creator: Sena, Andressa Souza
metadata.dc.contributor.advisor1: Nahime, Bacus de Oliveira
metadata.dc.contributor.advisor-co1: Felipe, Alexsandro dos Santos
metadata.dc.contributor.referee1: Akasaki, Jorge Luis
metadata.dc.contributor.referee2: Lima, Elton Carvalho de
metadata.dc.contributor.referee3: Alves, Michell Macedo
metadata.dc.description.resumo: O sistema de geração de energia renovável pelas caldeiras é utilizado amplamente nas indústrias e usinas de energia elétrica, sendo significativo seu consumo em todo o mundo. Nesse processo de geração de energia, é consumida biomassa e gerados resíduos, em grande parte não havendo um local apropriado para seu descarte. O presente trabalho buscou estudar o reaproveitamento de resíduos de madeira de eucalipto, proveniente da queima em caldeira de leito fluidizado de uma agroindústria, que produz, em média, 4.800 toneladas de resíduo/ano. O resíduo gerado não tem uma destinação ambientalmente correta, sendo muitas vezes armazenado no pátio da agroindústria e solos de lavouras. Com o objetivo de transformar o resíduo em blocos densos (briquetes), que sejam resistentes e duráveis para reutilizar em fornos e caldeiras, foram feitas análises das propriedades físico-químicas do resíduo como fluorescência de raio X (FRX) e difração de raios-X (DRX) para a análise de sua estrutura cristalina, tendo sido feita também a análise Termogravimétrica (TG) das amostras para avaliar a decomposição química do resíduo. Para a fabricação dos briquetes, o resíduo foi seco em estufa, algumas amostras foram prensadas em prensa universal e outras em prensa manual. Foi necessário fazer ajuste na umidade do material no momento da prensagem para conseguir formar o briquete. A umidade adicionada foi de 50% para os briquetes feitos na prensa universal aplicando pressões de 3,41 MPa, 5,10 MPa, 12,31 MPa e 37,50 MPa e de 74%, e para os briquetes feitos na prensa manual, aplicando pressão de 0,38 MPa. Após o processo de prensagem, foram feitos os ensaios de densidade aparente, durabilidade e queima. Com os resultados obtidos, foi possível avaliar a densidade e a pressão dos briquetes, sendo o briquete com menor densidade o que recebeu pressão de 0,38 MPa e o que obteve maior densidade o que recebeu pressão de 37,50 MPa. Em relação à durabilidade, o briquete com 37,50 MPa apresentou 92,4% de eficiência em relação aos outros briquetes, tendo uma perda de massa no ensaio de 7,6%. Os resultados das análises físico-químicas juntamente com as propriedades térmicas dos briquetes mostraram que o principal elemento presente na decomposição do resíduo é o CaCO3 (carbonato de cálcio), também foi possível verificar que a matéria orgânica está disponível no resíduo em grande quantidade, deste modo favorecendo a queima do briquete, concluindo que os briquetes produzidos são propícios para queima em caldeira e fornos, além de resistente aos transportes e ao armazenamento.
Abstract: The system of renewable energy generation by boilers is widely used in industries and in electric power plants, presenting significant consumption worldwide. In this process, biomass is consumed, generating waste without often having an appropriate place for disposal. This study aimed to analyze the reuse of waste from eucalyptus wood resulted from burning in a fluidized bed boiler of an agroindustry, which produces an average of 4,800 tons of waste per year. The waste generated is not going to an ecologically correct location, been often accumulated in some agroindustry company yard and crop soils. Waste physical and chemical properties, such as X-ray fluorescence (XRF) and X-ray diffraction (XRD), were analyzed for their crystalline structure to be transformed into dense, resistant, and durable blocks (briquettes) and to be reused in ovens and boilers. Thermogravimetric (TG) of the samples was also analyzed, evaluating the waste chemical decomposition. The residue was dried in an oven; some samples were pressed in a universal press and others in a manual press to manufacture the briquettes. It was needed to adjust the material moisture content when pressing, so that the briquette could be formed. Humidity of 50% was added to the briquettes made in the universal press, applying pressures of 3.41 MPa, 5.10 MPa, 12.31 MPa, and 37.50 MPa; 74% humidity was added for the briquettes made in the manual press, applying pressure of 0.38 MPa. After the pressing process, the tests of apparent density, durability, and firing were carried out. With the results found, it was possible to evaluate the briquette density and pressure; the briquette that received pressure of 0.38 MPa had a lower density and the one that received pressure of 37.50 MPa had a higher density. Regarding durability, the briquette with 37.50 MPa showed 92.4% efficiency in relation to the other briquettes, with a mass loss in the test of 7.6%. The analysis results on the physical-chemical characteristics together with the thermal properties of the briquettes showed that the main element present in the residue decomposition is CaCO3 (calcium carbonate); it was also possible to verify that the organic matter is available in great quantity in the residue, thus favoring the burning of the briquette. In conclusion, the produced briquettes are suitable for burning in boilers and ovens, in addition to being resistant for transport and storage.
Keywords: Resíduo de madeira de eucalipto, briquetes, agroindústria, sustentabilidade, energia renovável.
agroindustry, briquettes, eucalyptus wood waste, renewable energy, sustainability.
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL::MATERIAIS E COMPONENTES DE CONSTRUCAO
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Instituto Federal Goiano
metadata.dc.publisher.initials: IF Goiano
metadata.dc.publisher.department: Campus Rio Verde
metadata.dc.publisher.program: Programa de Pós-Graduação em Engenharia Aplicada e Sustentabilidade
metadata.dc.rights: Acesso Restrito
metadata.dc.rights.uri: http://creativecommons.org/licenses/by-nc-nd/3.0/br/
URI: https://repositorio.ifgoiano.edu.br/handle/prefix/1580
Issue Date: 17-Nov-2020
Appears in Collections:Mestrado em Engenharia Aplicada e Sustentabilidade

Files in This Item:
File Description SizeFormat 
dissertação_Andressa_Souza_Sena.pdf2,49 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons